Résumé du livre

L'OBJECTIF DE LA THESE EST DE DETERMINER LES CONDITIONS QUI MENENT A LA FORMATION DE GROSSES PARTICULES MONODISPERSES (DIAMETRE > 1 M) PAR POLYMERISATION EN DISPERSION DU STYRENE EN MILIEU HYDROALCOOLIQUE (PRINCIPALEMENT DES MELANGES ETHANOL/EAU), EN PRESENCE DE MACROMONOMERES A BASE DE POLY(OXYDE D'ETHYLENE) (POE) COMME STABILISANTS. CE MANUSCRIT EST DONC PRINCIPALEMENT CONSACRE A LA SYNTHESE ET LA CARACTERISATION DES MACROMONOMERES (QUI POURRONT COMPORTER DES PROPRIETES TENSIOACTIVES), ET A L'ETUDE DES MECANISMES DE LA POLYMERISATION EN DISPERSION DU STYRENE EN PRESENCE DE MACROMONOMERES. LA NUCLEATION ET LES CINETIQUES DE POLYMERISATION ONT ETE DECRITES DE FACON DETAILLEE. DE PLUS, UN PROGRAMME DE SIMULATION A ETE DEVELOPPE POUR DETERMINER LE PARTAGE DU STYRENE ET DE L'ETHANOL AU COURS DE LA POLYMERISATION. ENFIN, DIVERS FACTEURS INFLUENCANT L'INCORPORATION DU MACROMONOMERE A LA SURFACE DES PARTICULES ONT ETE ETUDIES: REACTIVITE DU MACROMONOMERE (MALEATES, METHACRYLATES, STYRENIQUES), STRUCTURE ET CONCENTRATION DU MACROMONOMERE, POLARITE DU SOLVANT, CONCENTRATION EN STYRENE, ETC. UN TAUX D'INCORPORATION DE 80%, AVEC UNE DENSITE DE GREFFAGE ELEVEE, A PU ETRE OBTENU AVEC UN MACROMONOMERE METHACRYLATE. EN OUTRE, L'EFFET DE LA DENSITE DE GREFFAGE SUR LA STABILITE DES PARTICULES A ETE EVALUE PAR ECHANGE DE SERUM ET PAR DES CYCLES GEL/DEGEL