Thermodynamic Data for Molybdenum Carbide and Tantalum Carbide

Résumé du livre

The heat capacity of dimolybdenum carbide (Mo2C) was measured from 51° to 298° K, and the entropy at 298.15° K was evaluated. Heat content measurements above 298.15° K were conducted for dimolybdenum carbide (MO2C) and monotantalum carbide (TaC). The results were combined with known heats of formation and the 298.15° K entropy for TaC to obtain values of heat and free energy of formation from 298.15° K to 1,400° K for Mo2C and from 298.15° K to 1,800° K for TaC.