Post-Irradiation Creep Properties of Cold-Worked 316 Stainless Steel As Measured with Small Creep Specimens
Auteur : M. Snykers, P. Van Asbroeck, W. Vandermeulen
Date de publication : 1986
Éditeur : ASTM International
Nombre de pages : 6
Résumé du livre
Small specimens (4 mm gage length, 1.3 mm diameter) of AISI 20% coldworked (CW) 316 stainless steel have been irradiated at 700°C up to 2 x 1022 n/cm2. Ageing at 650°C as well as irradiation caused a reduction in creep life and an increase in minimum creep rate as compared with as-received specimens. An investigation of a possible size effect indicated no difference between creep results obtained on these small specimens and on larger ones.